Discontinuous/non-uniform metal cap structure and process for interconnect integration

ABSTRACT

A method of fabricating an interconnect structure is provided which includes providing a dielectric material having a dielectric constant of about 3.0 or less and at least one conductive material embedded therein, the at least one conductive material has an upper surface that is coplanar with an upper surface of the dielectric material; and forming a noble metal-containing cap directly on the upper surface of the at least one conductive material, wherein the noble metal cap is discontinuous or non-uniform.

RELATED APPLICATION

This application is a divisional of U.S. Ser. No. 12/247,632, filed Oct.8, 2008, the entire contents of which are incorporated herein byreference.

BACKGROUND OF THE INVENTION

The present invention relates to semiconductor interconnect structures,and a method of fabricating the same. More particularly, the presentinvention relates to semiconductor interconnect structures havingenhanced electromigration (EM) resistance without degrading timedependent dielectric breakdown reliability.

FIELD OF THE INVENTION

Generally, semiconductor devices include a plurality of circuits thatform an integrated circuit (IC) fabricated on a semiconductor substrate.A complex network of signal paths will normally be routed to connect thecircuit elements distributed on the surface of the substrate. Efficientrouting of these signals across the device requires formation ofmultilevel or multilayered schemes, such as, for example, single or dualdamascene wiring structures. The wiring structure typically includescopper, Cu, since Cu based interconnects provide higher speed signaltransmission between large numbers of transistors on a complexsemiconductor chip as compared with aluminum, Al, based interconnects.

Within a typical interconnect structure, metal vias run perpendicular tothe semiconductor substrate and metal lines run parallel to thesemiconductor substrate. Further enhancement of the signal speed andreduction of signals in adjacent metal lines (known as “crosstalk”) areachieved in today's IC product chips by embedding the metal lines andmetal vias (e.g., conductive features) in a dielectric material having adielectric constant of less than 4.0.

In semiconductor interconnect structures, electromigration (EM) has beenidentified as one metal failure mechanism. Electromigration is thetransport of material caused by the gradual movement of the ions in aconductor due to the momentum transfer between conducting electrons anddiffusing metal atoms. The effect is important in applications wherehigh direct current densities are used, such as in microelectronics andrelated structures. As the structure size decreases, the practicalsignificance of EM increases.

EM is one of the worst reliability concerns for very large scaleintegrated (VLSI) circuits and manufacturing since the 1960's. Theproblem not only needs to be overcome during the process developmentperiod in order to qualify the process, but it also persists through thelifetime of the chip. Voids are created inside the metal conductors ofan interconnect structure due to metal ion movement caused by the highdensity of current flow.

Although the fast diffusion path in metal interconnects varies dependingon the overall integration scheme and materials used for chipfabrication, it has been observed that metal atoms, such as Cu atoms,transported along the metal/post planarized dielectric cap interfaceplay an important role on the EM lifetime projection. The EM initialvoids first nucleate at the metal/dielectric cap interface and then growin the direction to the bottom of the interconnect, which eventuallyresults in a circuit dead opening.

FIGS. 1A-1D are pictorial representations of a prior art interconnectstructure at various stages of an EM failure. In these drawings,reference numeral 12 denotes the dielectric cap, and reference numeral10 denotes the metal interconnect feature; all other components of theprior art interconnect structure are not labeled to avoid obscuring theEM problem. FIG. 1A is at an initial stress stage. FIG. 1B is at a timewhen void 14 nucleation initiates at the metal interconnect feature10/dielectric cap 12 interface. FIG. 1C is at a time when the void 14grows towards the bottom of the conductive feature 10, and FIG. 1D is ata time in which the void 14 growth crosses the metal interconnectfeature 10 causing a circuit dead opening.

It has been demonstrated that by replacing the Cu/dielectric interfacewith a Cu/metal interface can enhance electromigration resistance bygreater than 100×. Prior art metal caps are typically comprised of aCo-containing alloy such as, for example, CoWP, which is selectivelydeposited atop of the Cu conductor region of the interconnect structure.One problem with utilizing such selective deposited metal caps is thatsome of the metal cap extends onto the adjoining surface of theinterconnect dielectric material and, as such, electrical shorts betweenadjacent interconnects may arise. This is seen, for example, in FIG. 2wherein reference numeral 20 denotes a dielectric material, referencenumeral 22 denotes a conductive material embedded within the dielectricmaterial 20, reference numeral 24 denotes a Co-containing alloy metalcap, and reference numeral 25 denotes metal residues from theCo-containing alloy cap process.

In addition to the above, it is known to provide a metal cap directly onthe surface of an interconnect conductive material, such as, forexample, Cu, by recessing the interconnect conductive material below asurface of the interconnect dielectric material. Such a structure isshown, for example, in FIG. 3. In this figure, reference numeral 20denotes the interconnect dielectric material, reference numeral 22denotes the interconnect conductive material embedded within thedielectric material 20, reference numeral 23 denotes a dielectric cap,and reference numeral 24 denotes the metal cap. Although this prior artrecess process provides a metal cap that is located only on a surface ofthe recessed conductive material, such a process is problematic sincethere is high process cost associated therewith.

It is also worth mentioning that during a clean in dilute hydrofluoricacid, which is generally used to clean the surface of the interconnectdielectric material, corrosion of metal caps may occur. This isparticularly observed when CoWP is used as the metal cap material.

In view of the above, there is a continued need for providing aninterconnect structure in which the EM resistance is enhanced withoutdegrading the time dependent dielectric breakdown reliability of theinterconnect structure.

SUMMARY OF THE INVENTION

The present invention provides semiconductor interconnect structuresthat have improved EM reliability. The improved EM reliability isobtained without degrading the time dependent dielectric breakdownreliability of the interconnect structures. The present inventionfurther provides interconnect structures that have better reliabilityand technology extendibility for the semiconductor industry.

In one embodiment, the present invention provides an interconnectstructure in which a discontinuous noble metal-containing cap is presenton portions of an exposed upper surface of a non-recessed conductivematerial which is embedded within a low k dielectric material. The term“discontinuous” when referring to the noble metal-containing cap denotesthat the cap exists as nuclei or islands atop some portions of anexposed upper surface of the non-recessed conductive material.

In another embodiment of the present invention, an interconnectstructure is provided that includes a non-uniform noble metal-containingcap present on an exposed upper surface of a non-recessed conductivematerial which is embedded within a low k dielectric material. The term“non-uniform” when referring to the noble metal-containing cap denotesthat the cap has a rough source defined by a variable thickness acrossthe exposed upper surface of the embedded conductive material.

In both of the embodiments mentioned above, the noble metal-containingcap of the invention does not extend onto an exposed upper surface ofthe low k dielectric material. Preferably, the noble metal-containingcap of the invention does not extend onto an upper surface of adiffusion barrier that is used in separating the conductive materialfrom the low k dielectric material. The latter embodiment in which theinventive noble metal-containing cap does not extend onto an uppersurface of a diffusion barrier provides a structure that has improvedleakage control as compared with prior art interconnect structures.

In general terms, the present invention provides an interconnectstructure including:

a dielectric material having a dielectric constant of about 3.0 or lessand at least one conductive material embedded therein, the at least oneconductive material having an upper surface that is coplanar with anupper surface of the dielectric material; anda noble metal-containing cap present at least on some portion of theupper surface of the at least one conductive material, wherein saidnoble metal-containing cap is discontinuous or has a non-uniformthickness.

In the inventive structure, there is no “residues” from the noblemetal-containing cap deposited on the dielectric surface. By “residues”it is meant that no fragments of noble metal material form on thedielectric material surface. In some embodiments, the noblemetal-containing cap is not present on an upper surface of a diffusionbarrier that separates the at least one conductive material from thedielectric material.

The dielectric material which is present in the inventive interconnectstructure may be any interconnect dielectric material having adielectric constant of about 3.0 or less. Illustratively, the dielectricmaterial employed in the present invention comprises a silsesquioxane, aC doped oxide (i.e., an organosilicate) that includes at least atoms ofSi, C, O and H, a thermosetting polyarylene ether, or multilayersthereof. The dielectric material may be porous, non-porous or containregions and/or surfaces that are porous and other regions and/orsurfaces that are non-porous.

The conductive material which forms an embedded conductive region withinthe interconnect structure includes any material that has the ability totransfer electricity. Examples of conductive material that can bepresent in the conductive region include, for example, polySi, aconductive metal, a conductive metal alloy, a conductive metal silicideor combinations and multilayers thereof. In one embodiment of thepresent invention, the conductive material includes a conductive metalsuch as, for example, Cu, W, and/or Al. In a highly preferred embodimentof the present invention, the conductive material includes aCu-containing conductive material such as, for example, Cu, or a Cualloy (such as AlCu).

As mentioned above, the conductive material is separated from thedielectric material by a diffusion barrier. The diffusion barrierprevents diffusion of the conductive material into the dielectricmaterial. Examples of diffusion barriers that can be present within theconductive region include, for example, Ta, TaN, Ti, TiN, Ru, RuN, RuTa,RuTaN, IrTa, IrTaN, W, WN or combinations and multilayers thereof.

The conductive material may be present within a via opening, a lineopening, a combined via and line opening or any combination thereof.

The term “noble metal-containing” when referring to the cap locateddirectly atop the at least one conductive material includes any metalthat is resistant to corrosion or oxidation. The preferred noble metalsthat can be used in the present invention are selected from the groupconsisting of Ru, Ir, Rh, Pt, Co, W and alloys thereof. More preferably,the noble metal employed as the noble metal-containing cap comprises Ruor a Ru alloy.

In addition to the interconnect structure mentioned above, the presentinvention also provides a method of fabricating the same. In generalterms, the inventive method includes:

providing a dielectric material having a dielectric constant of about3.0 or less and at least one conductive material embedded therein, theat least one conductive material has an upper surface that is coplanarwith an upper surface of the dielectric material; andforming a noble metal-containing cap directly on the upper surface ofthe at least one conductive material, wherein the noble metal cap isdiscontinuous or non-uniform.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A-1D are pictorial representations (through cross sectionalviews) illustrating the formation of a circuit dead opening in a priorart interconnect structure which is caused by EM failure.

FIG. 2 is a prior art interconnect structure (through a cross sectionalview) including a Co-containing alloy metal cap located atop aconductive material that is embedded within a dielectric material, andmetal residues from the Co-containing alloy cap process are present onthe dielectric surface.

FIG. 3 is a prior interconnect structure (through a cross sectionalview) including a recessed conductive material embedded within adielectric material, said recessed conductive material having a metalcapping layer located thereon.

FIGS. 4A-4E are pictorial representations (through cross-sectionalviews) illustrating an interconnect structure that can be formed in thepresent invention containing a discontinuous noble metal-containing capatop a conductive material embedded within a dielectric material. It isnoted that FIGS. 4B-4E are cross-sectional views that are parallel tothe opening formed into the dielectric material.

FIG. 5 is a pictorial representation (through a cross-sectional viewthat is parallel to the opening formed into the dielectric material)illustrating an alternative interconnect structure that can be formed inthe present invention containing a non-uniform noble metal-containingcap atop a conductive material embedded within a dielectric material.

DETAILED DESCRIPTION OF THE INVENTION

The present invention, which provides interconnect structures havingenhanced electromigration (EM) resistance without degrading timedependent dielectric breakdown reliability and a method of forming thesame, will now be described in greater detail by referring to thefollowing discussion and drawings that accompany the presentapplication. It is noted that the drawings of the present applicationare provided for illustrative purposes only and, as such, the drawingsare not drawn to scale.

In the following description, numerous specific details are set forth,such as particular structures, components, materials, dimensions,processing steps and techniques, in order to provide a thoroughunderstanding of the present invention. However, it will be appreciatedby one of ordinary skill in the art that the invention may be practicedwithout these specific details. In other instances, well-knownstructures or processing steps have not been described in detail inorder to avoid obscuring the invention.

It will be understood that when an element as a layer, region orsubstrate is referred to as being “on” or “over” another element, it canbe directly on the other element or intervening elements may also bepresent. In contrast, when an element is referred to as being “directlyon” or “directly over” another element, there are no interveningelements present. It will also be understood that when an element isreferred to as being “connected” or “coupled” to another element, it canbe directly connected or coupled to the other element or interveningelements may be present. In contrast, when an element is referred to asbeing “directly connected” or “directly coupled” to another element,there are no intervening elements present.

As stated above, the present invention provides an interconnectstructure (See, for example, FIG. 4E and FIG. 5) including a dielectricmaterial having a dielectric constant of about 3.0 or less and having atleast one conductive material embedded therein. The at least oneconductive material has an upper surface that is coplanar with an uppersurface of the dielectric material. The inventive interconnect structurealso includes a noble metal-containing cap that is present at least onsome portion of the upper surface of the at least one conductivematerial. In one embodiment, the noble metal-containing cap isdiscontinuous, e.g., exists as nuclei or islands on the surface of theat least one conductive material. In another embodiment, the noblemetal-containing cap has a non-uniform thickness across the surface ofthe at least one conductive material.

In the inventive structure, there is no “residues” from the noblemetal-containing cap deposited on the dielectric surface. By “residues”it is meant that no fragments of noble metal material form on thedielectric material surface. In some embodiments, the noblemetal-containing cap is not present on an upper surface of a diffusionbarrier that separates the at least one conductive material from thedielectric material.

The present invention also provides a method of fabricating aninterconnect structure which includes a discontinuous/non-uniform noblemetal-containing cap. In general terms, the inventive method, which isillustrated, for example, in FIGS. 4A-4E, includes providing adielectric material having a dielectric constant of about 3.0 or lessand at least one conductive material embedded therein. The at least oneconductive material has an upper surface that is coplanar with an uppersurface of the dielectric material. Next, a noble metal-containing capis formed directly on the upper surface of the at least one conductivematerial. The noble metal-containing cap may be a discontinuous cap or anon-uniform cap that has a rough surface.

Specifically, FIG. 4A illustrates an initial structure 50 that can beemployed in the present invention in fabricating the inventiveinterconnect structure. The initial structure 50 includes a dielectricmaterial 52 having a pad stack 54 located on an upper surface thereof.

It is noted that the initial structure 50 is typically located upon asubstrate (not shown in the drawings of the present application). Thesubstrate may comprise a semiconducting material, an insulatingmaterial, a conductive material or any combination including multilayersthereof. When the substrate is comprised of a semiconducting material,any semiconductor such as Si, SiGe, SiGeC, SiC, Ge alloys, GaAs, InAs,InP and other III/V or II/VI compound semiconductors may be used. Inaddition to these listed types of semiconducting materials, the presentinvention also contemplates cases in which the semiconductor substrateis a layered semiconductor such as, for example, Si/SiGe, Si/SiC,silicon-on-insulators (SOIs) or silicon germanium-on-insulators (SGOIs).

When the substrate is an insulating material, the insulating materialcan be an organic insulator, an inorganic insulator or a combinationthereof including multilayers. When the substrate is a conductingmaterial, the substrate may include, for example, polySi, an elementalmetal, alloys of elemental metals, a metal silicide, a metal nitride orcombinations thereof including multilayers. When the substrate comprisesa semiconducting material, one or more semiconductor devices such as,for example, complementary metal oxide semiconductor (CMOS) devices canbe fabricated thereon.

When the substrate comprises a combination of an insulating material anda conductive material, the substrate may represent a first interconnectlevel of a multilayered interconnect structure.

The dielectric material 52 of the initial structure 50 comprises anyinterlevel or intralevel dielectric including inorganic dielectrics ororganic dielectrics. The dielectric material 52 may be porous,non-porous or contain regions and/or surfaces that are porous and otherregions and/or surfaces that may be non-porous. Some examples ofsuitable dielectrics that can be used as the dielectric material 52include, but are not limited to silsesquioxanes, C doped oxides (i.e.,organosilicates) that include atoms of Si, C, O and H, thermosettingpolyarylene ethers, or multilayers thereof. The term “polyarylene” isused in this application to denote aryl moieties or inertly substitutedaryl moieties which are linked together by bonds, fused rings, or inertlinking groups such as, for example, oxygen, sulfur, sulfone, sulfoxide,carbonyl and the like.

The dielectric material 52 typically has a dielectric constant that isabout 3.0 or less, with a dielectric constant of about 2.8 or less beingeven more typical. All dielectric constants mentioned herein arerelative to a vacuum, unless otherwise noted. These dielectricsgenerally have a lower parasitic cross talk as compared with dielectricmaterials that have a higher dielectric constant than 4.0. The thicknessof the dielectric material 52 may vary depending upon the dielectricmaterial used as well as the exact number of dielectric layers withinthe dielectric material 52. Typically, and for normal interconnectstructures, the dielectric material 52 has a thickness from 50 nm to1000 nm.

The dielectric material 52 is formed utilizing any conventionaldeposition process including, but not limited to chemical vapordeposition (CVD), plasma enhanced chemical vapor deposition (PECVD),evaporation, chemical solution deposition and spin-on coating.

After forming the dielectric material 52, pad stack 54 is formed on anexposed upper surface of dielectric material 52. The pad stack 54comprises an oxide, nitride, oxynitride or multilayers thereof (e.g., apad stack comprising a pad oxide and a pad nitride). The pad stack 54typically comprises a semiconductor oxide, semiconductor nitride and/ora semiconductor oxynitride. Preferably, the pad stack 54 comprises anoxide of silicon and/or a nitride of silicon.

In some embodiments, the pad stack 54 may be formed utilizing anyconventional deposition process including, for example, CVD, PECVD,evaporation, chemical solution deposition, physical vapor deposition(PVD) and atomic layer deposition (ALD). In other embodiments, the padstack 54 is formed by a thermal process such as, for example, a thermaloxidation, a thermal nitridation and/or a thermal oxynitridationprocess. In yet other embodiments, the pad stack 54 is formed utilizinga combination of deposition and thermal processes.

The thickness of the pad stack 54 may vary depending on the number ofmaterials within the pad stack itself as well as the technique that wasused in forming the same. Typically, the pad stack 54 has a thicknessfrom 10 nm to 80 nm.

After forming the initial structure 50 shown in FIG. 4A, at least oneopening 56 is formed into the dielectric material 52 utilizing the padstack 54 as a pattern mask. The resultant structure including the atleast one opening 56 is shown, for example, in FIG. 4B. The at least oneopening 56 may include a via opening, a line opening, a combined via andline opening, or any combination thereof. In the drawings, a lineopening is shown by way of a non-limiting example.

The at least one opening 56 is formed utilizing conventional lithographyand etching. The lithographic step includes forming a photoresist(organic, inorganic or hybrid) atop the pad stack 54 utilizing aconventional deposition process such as, for example, CVD, PECVD andspin-on coating. Following formation of the photoresist, the photoresistis exposed to a desired pattern of radiation. Next, the exposedphotoresist is developed utilizing a conventional resist developmentprocess.

After the development step, an etching step is performed to transfer thepattern from the patterned photoresist into first the pad stack 54 andthen the dielectric material 52. The patterned photoresist is typicallyremoved from the surface of the structure after transferring the patterninto the pad stack 54 utilizing a conventional resist stripping processsuch as, for example, ashing. The etching step used in forming the atleast one opening 56 comprises a dry etching process (including reactiveion etching, ion beam etching, plasma etching or laser ablation), a wetchemical etching process or any combination thereof. Typically, reactiveion etching is used to form the at least one opening 56.

Next, and as shown in FIG. 4C, a diffusion barrier 58 and a conductivematerial 60 are formed into each of the at least one openings 56. Thediffusion barrier 58 comprises Ta, TaN, Ti, TiN, Ru, RuN, RuTa, RuTaN,IrTa, IrTaN, W, WN or any other material that can serve as a barrier toprevent conductive material from diffusing there through. The thicknessof the diffusion barrier 58 may vary depending on the deposition processused as well as the material employed. Typically, the diffusion barrier58 has a thickness from 4 nm to 40 nm, with a thickness from 7 nm to 20nm being more typical.

The diffusion barrier 58, which is located between the conductivematerial 60 and the dielectric material 52 is formed by any conventionaldeposition process including, for example, CVD, PECVD, PVD, sputteringand plating.

The conductive material 60 used in forming the conductive region of theinterconnect structure includes, for example, polySi, a conductivemetal, an alloy comprising at least one conductive metal, a conductivemetal silicide or combinations thereof. Preferably, the conductivematerial 60 that is used in forming the conductive region is aconductive metal such as Cu, W or Al, with Cu or a Cu alloy (such asAlCu) being highly preferred in the present invention.

The conductive material 60 is formed into each of the openings 56 thatare lined with the diffusion barrier 58 utilizing any conventionaldeposition process including, for example, CVD, PECVD, PVD, sputtering,plating, chemical solution deposition and electroless plating. Afterdeposition of the conductive material 60, the structure is subjected toa planarization process such as, for example, chemical mechanicalpolishing (CMP) and/or grinding. The planarization process provides aplanar structure such as is shown in FIG. 4C in which the upper surfacesof the dielectric material 52, the diffusion barrier 58 (which is nowU-shaped) and the conductive material 60 are substantially coplanar witheach other. It is noted that during the planarization process, theremaining pad stack 54 is removed from the structure.

Next, and as is shown in FIG. 4D, a discontinuous noble metal-containingcap 62 is selectively formed essentially atop the conductive material60. The term “noble metal-containing” when referring to thediscontinuous noble metal cap 62 located essentially atop the at leastone conductive region (i.e., conductive material 60) includes any metalthat is resistant to corrosion or oxidation. The term “essentially” whenreferring to the discontinuous noble metal-containing cap 62 is usedherein to denote that no portion of the cap extends onto the surface ofthe dielectric material. Preferably, no portion of the cap 62 extendsonto the diffusion barrier.

The preferred noble metals that can be used in the present invention asthe discontinuous noble metal-containing cap 62 are selected from thegroup consisting of Ru, Ir, Rh, Pt, Co, W and alloys thereof. The term“alloy” is used to denote a mixture of noble metals as well as elementssuch as W, B and P. More preferably, the noble metal employed as thediscontinuous noble metal-containing cap 62 comprises Ru or a Ru alloy.In some embodiments, the discontinuous noble metal-containing cap 62includes a multilayered noble metal or noble metal alloy stack.

The thickness of the discontinuous noble metal-containing cap 62 mayvary depending on the type of noble metal present in the cap, thedeposition technique and conditions used as well as the number of noblemetals within the cap. Typically, the discontinuous noblemetal-containing cap 62 has a thickness from 1 Å to 100 Å, with athickness from 5 Å to 50 Å being more highly preferred.

In some embodiments of the present invention, the discontinuousmetal-containing cap 62 is formed by a chemical deposition processincluding, for example, CVD, PECVD and ALD. When a chemical depositionprocess is used in forming the discontinuous noble metal-containing cap62, the discontinuity within the cap is achieved by controlling at leastone of the deposition time, the deposition pressure and the depositiontemperature.

Specifically, the applicants have determined that a discontinuous noblemetal-containing cap, as described above, can be obtained by performingthe chemical deposition using at least one of the following depositionparameters: A deposition time of less than 3 minutes, preferably from0.1 minutes to 2 minutes, and more preferably from 0.5 minutes to 1minute. A deposition pressure of 50 mTorr or less, preferably 20 mTorror less, and more preferably from 5 mTorr to 20 mTorr. A depositiontemperature of 300° C. or less, preferably 200° C. or less, and morepreferably from 150° C. to 200° C. In a highly preferred embodiment ofthe invention, a discontinuous noble metal-containing cap 62 can beobtained by chemical deposition at a temperature from 150° C. to 200° C.and a pressure from 5 mTorr to 20 mTorr for a duration of less than 1minute.

In addition to chemical deposition, a discontinuous noblemetal-containing cap 62 can be formed by utilizing electroless platingor by electroplating. Electroplating is a process of using electricalcurrent to reduce cations of a desired material, e.g., a noble metal,from a solution and coat a conductive object, e.g., the at least oneconductive material, with a thin layer of the material, e.g., the noblemetal. In electroless plating, a redox reaction involving the oxidationof one or more soluble reducing agents such as, for example,hypophosphite, and the reduction of one or metallic ions, e.g., noblemetal ions, occurs on the surface of a substrate, e.g., the at least oneconductive material.

When plating techniques are used in forming a discontinuous cap, thediscontinuity within the cap is achieved by performing the platingprocess for a duration of time of less than 3 minutes, preferably from0.1 minutes to 2 minutes, and more preferably from 0.5 minutes to 1minute. The plating temperature and pressure are not relative for thisembodiment for controlling the discontinuity of the cap 62.

In addition to the above techniques that have been described, thediscontinuous noble metal-containing cap 62 can be formed by firstforming a continuous noble metal-containing cap across the entiresurface of the at least one conductive material; some of the noble metalcap may extend onto an upper surface of the diffusion barrier, but notonto the dielectric material. Such deposition is achieved utilizing alow temperature chemical deposition process including, for example, CVD,PECVD, low pressure CVD and ALD. By “low temperature”, it is meant adeposition temperature of about 200° C. or less, with a depositiontemperature of less than about 150° C. being even more preferred. Thedeposition conditions are selected to provide a deposition rate of thecontinuous noble metal-containing cap onto the conductive material 60that is from 0.2 to 1.2 Å/sec.

After forming the continuous noble metal-containing cap, portions of thecontinuous noble metal-containing cap are selectively removed so as toform a discontinuous noble metal-containing cap, as described above. Theselective removal may be performed by first forming a patterned mask orblock mask over portions of the structure, including portions of thecontinuous noble metal-containing cap. Next, a selective etching processincluding, for example, a dry etch or a wet chemical etch can be used.When dry etching is used, one of reactive ion etching, ion beam etching,plasma etching and laser ablation can be used. When a wet chemical etchis employed, a mixture of HCl, H₂SO₄, HF and HNO₃ can be used as achemical etchant. In yet another embodiment, the selective removal canbe achieved using a touch-up chemical mechanical polishing (CMP)process. By “touch-up CMP” it is meant a short, less than 1 minute, andnon-uniform CMP process.

After selectively forming the discontinuous noble metal-containing cap62 predominately onto conductive material 60, a dielectric capping layer64 is formed across the entire structure shown in FIG. 4D. The resultantstructure including the dielectric capping layer 64 is shown, forexample, in FIG. 4E. The dielectric capping layer 64 comprises anysuitable dielectric capping material such as, for example, SiC, Si₄NH₃,SiO₂, a carbon doped oxide, a nitrogen and hydrogen doped siliconcarbide SiC(N,H) or multilayers thereof.

The thickness of the dielectric capping layer 64 may vary depending onthe technique used to form the same as well as the material make-up ofthe layer. Typically, the dielectric capping layer 64 has a thicknessfrom 15 nm to 100 nm, with a thickness from 25 nm to 45 nm being moretypical.

The dielectric capping layer 64 is formed utilizing any conventionaldeposition process including, for example, CVD, PECVD, evaporation,spin-on coating and chemical solution deposition.

FIG. 4E illustrates an interconnect structure in accordance with anembodiment of the present invention. Specifically, this inventiveinterconnect structure includes a dielectric material 52 having adielectric constant of about 3.0 or less. The dielectric material 52 hasat least one conductive region (represented by conductive material 60)embedded within the dielectric material 52, said at least one conductiveregion having an upper surface. A discontinuous noble metal cap 62 islocated directly on the upper surface of the at least one conductiveregion (i.e., conductive material 60).

FIG. 5 illustrates an alternative interconnect structure that can beemployed in the present invention. The alternative interconnectstructure of FIG. 5 is essentially the same as the interconnectstructure shown in FIG. 4E, except that the discontinuous noblemetal-containing cap 62 is replaced with a noble metal cap that has arough surface that is characterized as having a variable thicknessacross the entire surface of the at least one conductive material. Inthe alternative interconnect structure, reference numeral 62′ is used todenote the ‘non-uniform’ noble metal-containing cap. The non-uniformnoble metal-containing cap 62′ is formed utilizing basically the samechemical deposition techniques and materials as described above. Onedifference between the above described chemical depositions techniquesthat ensures a non-uniform noble metal-containing cap 62′ is that longerprocessing times are used. For example, a non-uniform noblemetal-containing cap 62′ can be formed using a desposition time of lessthan 5 minutes, preferably from 0.5 to 3 minutes, and more preferablyfrom 1 minute to 2 minutes.

Notwithstanding whether a discontinuous or non-uniform noblemetal-containing cap is formed, the applicants have determined that thepresence of either the discontinuous noble metal-containing cap or thenon-uniform noble metal-containing cap atop a conductive materialembedded within an interconnect dielectric improves the EM resistance ofthe interconnect structure. In prior art interconnect structures, acontinuous noble metal-containing cap is used and was thought to be thedesired cap design for EM improvement. In addition to improved EM, theapplicants have determined that the presence of either the discontinuousnoble metal-containing cap or the non-uniform noble metal-containing capatop a conductive material embedded within an interconnect dielectricalso improves the time dependent dielectric breakdown (TDDB) reliabilityof the interconnect structure. Such an improved in TDDB reliability isnot observed when a continuous noble metal-containing cap is employed.

While the present invention has been particularly shown and describedwith respect to preferred embodiments thereof, it will be understood bythose skilled in the art that the foregoing and other changes in formsand details may be made without departing from the spirit and scope ofthe present invention. It is therefore intended that the presentinvention not be limited to the exact forms and details described andillustrated, but fall within the scope of the appended claims.

What is claimed is:
 1. A method of fabricating an interconnect structurecomprising: providing a dielectric material having a dielectric constantof about 3.0 or less and at least one conductive material embeddedtherein, the at least one conductive material has an upper surface thatis coplanar with an upper surface of the dielectric material; andforming a noble metal-containing cap directly on the upper surface ofthe at least one conductive material, wherein said forming the noblemetal-containing cap comprises forming a continuous noblemetal-containing cap across the entire upper surface of the at least oneconductive material utilizing a deposition temperature of about 200° C.or less, and selectively removing portions of the continuous noblemetal-containing cap to form the discontinuous or non-uniform noblemetal-containing cap, wherein selectively removing includes a touch-upchemical mechanical polishing process.
 2. The method of claim 1 whereinsaid forming said noble metal-containing cap is selected from the groupconsisting of chemical vapor deposition (CVD), plasma enhanced chemicalvapor deposition (PECVD), atomic layer deposition (ALD), electrolessplating and electroplating.
 3. The method of claim 2 wherein saidforming the noble metal-containing cap includes one of CVD, PECVD andALD.
 4. The method of claim 3 wherein said deposition is performed at adeposition time of less than 3 minutes.
 5. The method of claim 3 whereinsaid deposition is performed at a deposition pressure of 50 mTorr orless.
 6. The method of claim 3 wherein said deposition is performed at adeposition time of less than 3 minutes, and a deposition pressure of 50mTorr or less.
 7. The method of claim 3 wherein said deposition isperformed at a temperature from 150° C. to 200° C. and a pressure from 5mTorr to 20 mTorr for a duration of less than 1 minute.
 8. The method ofclaim 1 further comprising forming a dielectric capping layer atoplocated atop the dielectric material and the noble metal-containing cap.9. The method of claim 1 wherein said noble metal-containing cap isdiscontinuous.
 10. The method of claim 1 wherein said forming the noblemetal-containing cap includes selecting a metal from the groupconsisting of Ru, Ir, Rh, Pt, Co, and W.
 11. The method of claim 10wherein said metal further includes one of W, B and P.
 12. The method ofclaim 1 wherein said forming the noble metal-containing cap comprises aplating technique that is performed for a duration of less than 3minutes.
 13. The method of claim 1 wherein said forming the noblemetal-containing cap includes deposition of a metal at a deposition ratethat is from 0.1 to 1.2 Angstroms/second.
 14. The method of claim 1wherein said noble metal-containing cap has sidewall edges that arecoincident to sidewall surfaces of said at least one conductivematerial.
 15. The method of claim 1 wherein said deposition is performedat a deposition pressure of 50 mTorr or less.